Synthesis of a magnetic core–shell carbon nanotube@MgNi2FeO4.5 nanotube composite

Yong Cao, Yixin Wang, Ziming Dong, Xiangyang Zhang, Chenhao Xiao, and Guoting Li

North China University of Water Resources and Electric Power, Zhengzhou, People’s Republic of China

 

E-mail: caoyangel@126.com

Abstract: In this paper, a magnetic core–shell composite with MgNi2FeO4.5 nanotubes as core and carbon nanotubes (CNTs) as shell was synthesized by in situ growth of CNTs on the surface of MgNi2FeO4.5 nanotubes via a catalytic chemical vapor deposition method. The MgNi2FeO4.5 nanotubes were prepared using a mixed aqueous solution of Mg(NO3)2, Ni(NO3)2 and Fe(NO3)3 (molar ratio of 1:2:1) and anodic aluminum oxide as template. Both the growth temperature and time of CNTs brought about effect on the structure and magnetic property of the composite were investigated. X-ray diffraction, transmission electron microscope, field emission scanning electron microscope, Raman spectroscopy and vibrating sample magnetometer were used to characterize the as-prepared samples. The MgNi2FeO4.5 nanotubes are parallel arranged, and the exterior surface of which is wrapped by CNTs when the growth temperature exceeding 480 °C. Magnetic measurement demonstrates the composite with higher growth temperature and shorter growth time possesses more excellent magnetic property.

Keywords: Carbon nanotubes ; MgNi2FeO4.5 nanotubes ; Chemical vapor deposition ; Magnetic property 

Full paper is available at www.springerlink.com.

DOI: 10.1007/s11696-019-00867-x

 

Chemical Papers 74 (1) 175–182 (2020)

Wednesday, December 11, 2024

IMPACT FACTOR 2023
2.1
SCImago Journal Rank 2023
0.381
SEARCH
Advanced
VOLUMES
© 2024 Chemical Papers